Haynes 214 is a Nickel-Chromium-Aluminium-Iron alloy which is principally intended for use at temperatures of 955°C (1750°F) and above. It exhibits resistance to oxidation that far exceeds virtually all conventional heat resistant wrought alloys at these temperatures.
Click to find out more about each profile type
.001” (0.025 mm) çaplarda
.827” (21 mm) çaplarda
Bobin, makara ve belirli uzunluklarda kesilmiş / çubuk halde teller.
.0015" (0.3mm) çaplarda
.787" (20mm) çaplarda
Bobin, makara ve belirli uzunluklarda kesilmiş / çubuk halde teller.
.0157" (0.4mm) çaplarda
.394" (10mm) çaplarda
Bobin, makara ve belirli uzunluklarda kesilmiş / çubuk halde teller.
Resistance to oxidation that far exceeds most heat resistant alloys at temperatures of 955ºC (1750ºF) and above. High temperature static applications **
Tanımlar
Condition | Yakl. çekme mukavemeti | Yaklaşık. çalışma sıcaklığı depending on load** and environment | ||
N/mm² | ksi | °C | °F | |
Annealed | 900 – 1200 | 131 – 174 | -200 to +1100 | -330 to +2010 |
Spring Temper | 1300 – 1700 | 189 – 247 | -200 to +1100 | -330 to +2010 |
˘ Haynes International’ın ticari adı
** Statik uygulamalar = durağan/sabit/hareketsiz/katı